High Strength Galvanized Steel Core Wire Heavy Zinc Coating Greased For ACSR ASTM B498

High Strength Galvanized Steel Core Wire Heavy Zinc Coating Greased For ACSR ASTM B498

  • हाई लाइट

    steel core wire rope

    ,

    steel stranded wire

  • Steel Grade
    High Carbon Wire Rod
  • Wire Gauge
    1.0-4.8mm
  • Type
    Galvanized
  • Alloy Or Not
    Non-alloy
  • Special Use
    Free Cutting Steel
  • Application
    ACSR, Ground Wire, Suspension Bracket, Communication Cable, Stay Wire.
  • Standard
    AISI|ASTM|BS|DIN|GB|JIS
  • Place of Origin
    Anhui,China
  • ब्रांड नाम
    Litong Global
  • प्रमाणन
    ISO9001-2008
  • Model Number
    LT-058
  • Minimum Order Quantity
    Negotiable
  • मूल्य
    Negotiable
  • Packaging Details
    Standard export packing on drum
  • Supply Ability
    400tons/day

High Strength Galvanized Steel Core Wire Heavy Zinc Coating Greased For ACSR ASTM B498

Description
Our galvanized stranded wires provide a combination of superior properties compared to conventional six strand ropes. With compacted structure and smooth face, this 1*7 galvanized stranded wire provides enhanced durability and resistance to abrasion and crushing, and improves the service life.

Construction & Diameter: 1*7/4.8-12.7 mm

Features
1. The galvanized stranded wire offers a smooth and polished surface.
2. It offers excellent antirust performance.
3. It is adhesive and flexible.

Application
Our 1*7 galvanized stranded wire can be used as messenger wires, guy wires, core wires or strength members, earth wires/ground wires, barrier cables, structure cables, messenger wires for optical fiber cable, etc.

As a professional 1*7 galvanized stranded wire manufacturer and supplier based in China, We also offers1*3, 1*19 galvanized stranded wire, 12.70mm PC strand, 2.0mm and 2.64mm galvanized steel wire, among others.

EN 50189 Standard

Table 1. Initial Settings for Determining Stress 1% Extension
Nominal Wire Diameter, mm Initial Stress, N/mm2 Initial setting of extensometer for a gauge length of 250mm2
1.24 2.25 100 0.125
2.25 3 200 0.25
3 4.75 300 0.375
4.75 5.5 400 0.5
For other gauge lengths, multiply the initial setting by the gauge length in mm divided by 250.

 

Table 2. Zinc Coating Requirements
Nominal Wire Diameter, mm Class A Class B Class C Class D Class E
Over Up to and incl. Min. mass of Zn g/m2 Min. no. of one minute dips Min. mass of Zn g/m2 Min. no. of one minute dips Min. mass of Zn g/m2 Min. no. of one minute dips Min. mass of Zn g/m2 Min. no. of one minute dips Min. mass of Zn g/m2 Min. no. of one minute dips
1.24 1.5 185 2 370 3.5 150 1 365 3 185 2
1.5 1.75 200 2 400 3.5 160 1.5 460 3.5 200 2
1.75 2 215 2.5 430 4 175 2 550 4 215 2.5
2 2.25 215 2.5 430 4 175 2 550 4 250 3.5
2.25 2.75 230 3 460 4 190 2.5 640 5 250 3.5
2.75 3 230 3 460 4 190 2.5 640 5 250 3.5
3 3.5 245 3.5 490 4 205 3 730 6 250 3.5
3.5 4.25 260 3.5 520 4 260 3.5 730 6 260 3.5
4.25 4.75 275 4 550 4 275 4 775 6 275 4
4.75 5 200 4 580 5 290 4 825 6 290 4
5 5.25 290 4 580 5 290 4 825 6 290 4
5.25 5.5 290 4 580 5 290 4 825 6 290 4

 

Table 3. Mechanical Properties of ST1A Wires
Nominal wire diameter mm Diameter tolerance Stress at 1% extension, MPa Tensile strength, MPa Elongation on 250mm Mandrel diameter for wrapping test No. of torsion twists
Over Up to and incl. mm N/MM2 N/MM2 %
Min. Min. Min. xd Min.
1.24 1.5 ±0.03 1170 1400 3 1 18
1.5 1.75 ±0.03 1170 1400 3 1 18
1.75 2.25 ±0.03 1170 1400 3 1 18
2.25 2.75 ±0.04 1140 1350 3 1 16
2.75 3 ±0.05 1140 1350 3.5 1 16
3 3.5 ±0.05 1100 1300 3.5 1 14
3.5 4.25 ±0.06 1100 1300 4 1 12
4.25 4.75 ±0.06 1100 1300 4 1 12
4.75 5.5 ±0.07 1100 1300 4 1 12

 

Table 4. Mechanical properties of ST2B Wires
Nominal wire diameter mm Diameter tolerance Stress at 1% extension, MPa Tensile strength, MPa Elongation on 250mm Mandrel diameter for wrapping test
Over Up to and incl. mm N/MM2 N/MM2
1.24 1.5 ±0.05 1100 1300 4 1
1.5 1.75 ±0.05 1100 1300 4 1
1.75 2.25 ±0.05 1100 1300 4 1
2.25 2.75 ±0.06 1070 1250 4 1
2.75 3 ±0.06 1070 1250 4 1
3 3.5 ±0.07 1000 1200 4 1
3.5 4.25 ±0.09 1000 1200 4 1
4.25 4.75 ±0.10 1000 1200 4 1
4.75 5.5 ±0.11 1000 1200 4 1

Other Products

 

BS4565-1990 Standard

Table 1. Initial Settings for Determining Stress 1% Extension
Nominal Diameter of Galvanized Steel Wire Initial Stress N/mm2 Initial Setting of Extensometer mm/mm
> <
mm mm
1.18 2.24 95 0.05
2.24 3.15 190 0.10
3.15 5.00 285 0.15

 

Table 2. Tensile Strength and Stress at 1% Elongation
Nominal Diameter of Galvanized Steel Wire Tensile Strength minimum N/mm2 Stress at 1% elongation minimum N/mm2
> <
mm mm
1.18 2.24 1400 1180
2.24 3.15 1320 1140
3.15 5.00 1320 1100

 

Table 3. Properties for High Strength Galvanized Steel Wire for ACSR
Tensile strength grade N/mm2, min. 1550 1700 1800
Nominal diameter of galvanized wire Min. stress at 1% elongation Min. elongation L0+=200mm% Steel wrap test dia. Min. stress at 1% elongation Min. elongation L0+=200mm% Steel Wrap test dia. Min. stress at 1% elongation Min. elongation L0+=200mm% Steel wrap test dia.
>
mm mm
1.18 1.32 1260 3.0 1d 1320 3.0 2d 1370 3.0 3d
1.32 1.80 1260 3.5 1d 1320 3.0 2d 1370 3.0 3d
1.80 2.24 1260 3.5 2d 1320 3.0 2d 1370 3.0 3d
2.24 2.72 1260 3.5 2d 1320 3.5 3d 1370 3.0 3d
2.72 2.90 1260 3.5 2d 1320 3.5 3d 1370 3.0 3d
2.90 4.00 1220 4.0 3d 1280 3.5 3d - - -
4.00 5.00 1220 4.0 3d - - - - - -
d=Nominal diameter of galvanized wire
L0= Original Gauge Length

 

Table 4. Conversions of Tensile Strength and Stress at 1% Elongation
N/MM2 tonf/in2
1100 71.2
1140 73.8
1180 76.4
1220 79.0
1260 81.6
1280 82.9
1320 85.5
1370 88.7
1400 9.07
1550 100.4
1700 110.1
1800 116.6

 

ASTMB498B/498M-2002 Standard

Table 1. Zinc Coating
Specified Diameter of Coated Wre Class A   Class C
1.6-1.9 210   630
>1.9-2.3 220 440 660
>2.3-2.7 230 460 690
>2.7-3.1 240 480 720
>3.1-3.5 260 520 780
>3.5-3.9 270 540 810
>3.9-4.5 275 550 825
>4.5-4.8 300 600 900

 

Table 2. Tensile Requirements
Specified Diameter Stress at 1 % Extension min Mpa Ultimate Tensile Strength min MPA Elongation in 250mm, min, 1%
Class A Class B Class C Class A Class B Class C Class A Class B Class C
1.6-2.3 1310 1240 1170 1450 1380 1310 3 3 3
>2.3-3.05 1280 1210 1140 1410 1340 1280 3.5 3 3
>3.05-3.6 1240 1170 1100 1410 1340 1280 4 3 3
>3.6-4.8 1170 1100 1070 1380 1280 1240 4 4 4

 

Table 3. Initial Settings for Determining Stress 1% Extension
Specified Diameter, mm Initial Stress, MPA Initial Setting of Extensometer, mm/mm
1.6-2.3 100 0.0005(0.05% extension)
>2.3-3.05 190 0.0010(0.10% extension)
>3.05-4.8 290 0.0015(0.15% extension)

 

Table 4. Mandrel Size for Adherence Test
Specified Wire Diameter,mm Ratio of Mandrel Diameter to Wire Diameter
1.6-2.3 3
>2.3-3.05 4
>3.05-4.8 5

 

Table 5. Permissible Variations in Diameter of Zinc-Coated Steel Wire
Specified Diameter, mm Permissible Variation, mm
Plus Minus
1.6-2.3 0.04 0.03
>2.3-3.05 0.05 0.05
>3.05-3.6 0.08 0.05
>3.6-4.8 0.1 0.08

Other Products

ASTM A475 Standard

 

Dia. of strand, in(mm) Minimum Breaking Strength of Strand,1bf(kN) Weight of Zine Coating, g/m2
High Strength Grade Extra High Strength Grade CLASS A
3/16(4.76) 2850(12.677) 3990(17.748) 153
1/4(6.35) 2850(21.129) 6650(29.581) 183
5/16(7.94) 8000(35.586) 11200(49.820) 244
3/8(9.52) 10800(48.040) 15400(68.503) 259
7/16(11.11) 14500(64.499) 20800(92.523) 275
1/2(12.70) 18800(83.627) 26900(119.657) 275

 

ASTM B498 Standard

Dia of Wire, mm Tensile Strength, Mpa Stress at 1% Extension, Mpa Coating, g/m2
CLASS A CLASS B
0.80-1.57 1000-1550 / 50-153 /
1.57-1.90 1000-1550 / 153-210 /
1.90-2.30 1000-1550 1310 220 440
2.30-2.70 1000-1550 1280 230 460
2.70-3.10 1000-1550 1280 240 480
3.10-3.50 1000-1550 1240 260 520
3.50-3.90 1000-1550 1170 270 540
3.90-4.50 1000-1550 1170 275 550
4.50-4.80 1000-1550 1170 300

 